Trouble Shooting
Molded Part Cracking
Others
Destruction of painted products
| Cause | External force and inferior paint characteristics (for impact and extension) |
|---|---|
| Countermeasures |
|
Fracture of Plated Parts
| Cause | External force and inferior plating characteristics (for impact and extension) |
|---|---|
| Countermeasures |
|
Fracture due to deterioration of material properties
| cause(1) | Mixing of different materials |
|---|---|
| Countermeasures | Eliminate the cause of mixing |
| Cause (2) | Deterioration as a result of weathering or light |
| Countermeasures | Use materials with good weather resistance |
| Cause(3) | Thermal degradation |
| Countermeasures | Use materials with good thermal properties |
| Cause(4) | Thermal degradation in the cylinder |
| Countermeasures | Ensure that conditions are suitable for molding |
Fracture due to usage of materials with poor impact characteristics
| Cause | External force and low-strength molded parts |
|---|---|
| Countermeasures | Switch to materials with high impact strength |
Fracture at low temperatures
| Cause | External force and a drop in molded part strength |
|---|---|
| Countermeasures | Switch to materials with high impact strength |
Creep fracture
| Cause | Application of loading over an extended period of time |
|---|---|
| Countermeasures | Reduce initial deformation and load Increase the modulus of section Reduce the stress |